This study presents a comparative analysis of specimens before and after photochemical and electrochemical ageing processes. The specimens were cut out of the pipes obtained through extrusion. The examinations were carried out for two commercial grades of polyethylene. Ageing with UV radiation was carried out using a gas discharge lamp, whereas simulation of electrochemical ageing was performed in a water solution of NaCl. Tensile strength testing, differential scanning calorimetry, colour and gloss measurements and hardness testing using the method of ball indentation were carried out for both types of specimens (after ageing and without ageing). Analysis of the results of the examinations revealed that ageing caused significant changes in properties of the specimens. In the samples after ageing was observed decrease in tensile strength. Found a decrease in the degree of crystallinity and changing temperatures physical changes. In the samples after ageing was observed different values of the parameters describing the colour. In samples after ageing also reported a reduction in gloss and hardness. (original abstract)
Twórcy
autor
- Częstochowa University of Technology
autor
- Częstochowa University of Technology
Bibliografia
- Brabowska B., Biodegradacja tworzyw polimerowych, "Archives of Foundry Engineering" 10 (2010) 57-60.
- Czaja K., Poliolefiny, WNT, Warszawa, 2005.
- Dobkowski Z., Lifetime prediction for polymer materials using OIT measurements by the DSC method, "Polimery", 3 (2005) 213-215.
- EL-Nouby M., M. El Shazy, Attenuation of UV-B radiation in the atmosphere: Clouds effect, at Qena (Egypt), "Atmospheric Environment", 41 (2007) 4856-4864.
- Gnatowski A., Badania struktury i właściwości termicznych polietylenu i kompozytów polietylenu z włóknem tekturowym po procesach wygrzewania i starzenia promieniami UV, "Composites. Theory and Practice" (2009) 3 238-243.
- Gnatowski A., Influence of injection moulding conditio and annealing on thermal properties, structure, color and gloss of composite polyamide 6 with glass beads, "Composites. Theory and Practice", 2, (2012) 115-120.
- Jachowicz T., A. Krzyżak, Wpływ starzenia naturalnego na wybrane właściwości rur z polietylenu, "Matrol" (2009) 70-76.
- Joao F., N. Eduardo, P. Amauri, J. Soares, Modeling hourly and daily fractions of UV, PAR and NIR to global solar radiation under various sky conditions at Botucatu, Brazil, "Applied Energy", 86 (2009) 299-309.
- Kwacz M., J. Zadrosz, Przykłady zastosowań rur z tworzyw sztucznych w sieciach podziemnych cz. II, "Nowoczesne Budownictwo Inżynieryjne", 3 (2008) 66-71.
- Maity M., B.B. Khatua, C.K. Das, Effect of processing on the thermal stability of the blends based on polyurethane, "Polymer degradation and stability", 72 (2001) 499-503.
- Molenda J., M. Wrona, E. Siwiec, Zastosowanie modelu CIE lab w badaniach barwy lotnych popiołów, "Problemy Eksploatacji", 3 (2012) 177-187.
- Piekarska E., Rury z polietylenu - niezawodność funkcjonowania w wodociągach, sieciach paliw gazowych i kanalizacji, "Przetwórstwo Tworzyw", 2 (2008) 39-44.
- Pusz A., K. Michalik, Creep damage mechanisms in gas pipes made of high density polyethylene, "Archives of Materials Science and Engineering", 2 (2009) 89-95.
- Sobków D., K. Czaja, Wpływ warunków przyspieszonego starzenia na proces degradacji poliolefin, "Polimery", 9 (2003) 627-632.
Typ dokumentu
Bibliografia
Identyfikatory
Identyfikator YADDA
bwmeta1.element.ekon-element-000171428245